Fa'atau atu o le paipa u'amea 40Cr mo le gaosiga
40Cr paipa uʻamea o se ituaiga uʻamea lapotopoto ma vaega gaogao ma leai sooga faataamilo. E faia i le paipa malo avanoa e ala i le perforation, ona faia lea o le taʻavale vevela, taʻavale malulu poʻo le ata malulu. Pe a faatusatusa i le uamea lapotopoto ma isi uamea malo, pe a tutusa le punou ma le malosi torsional, o le mamafa o le paipa uamea e mama, o se ituaiga o vaega tau tamaoaiga.
E tusa ai ma GB / T 3077-2008: tuufaatasiga kemikolo (vaega vaega tele,%) C 0.37 ~ 0.44, Si 0.17 ~ 0.37, Mn 0.50 ~ 0.80, cr0.80 ~ 1.10, Ni ≤ 0.30【 Mechanical meatotino]
Fa'ata'ita'i avanoa avanoa (mm): 25
vevela vevela o le tineia muamua (℃): 850; Fa'alili: Suau'u
Fa'avevela lona lua vevela vevela (℃):-
Tempering vevela vevela (℃): 520; Coolant: vai, suauu
Malosi'i (σ b/MPa): ≧980
Tu'uga fa'atosina (σ s/MPa): ≧785
Elongation ina ua gau(δ 5/%): ≧9
Fa'aitiitiga o vaega(ψ/%): ≧45
Malosi'i fa'a'a'afiaga (aku2/J): ≥ 47
Malosi o le Brinell (hbs100 / 3000) (fa'afefete po'o le vevela maualuga): ≤ 207
O togi u'amea masani o GB i Saina o 40Cr, mea DIN Numera 1.17035 / 1.7045, DIN 41Cr4 / 42gr4, en 18, BS 41Cr4, AFNOR 42c4, NF 38cr4 / 41Cr4, uni 41Cr4 / 41Cr4, DIN 41Cr4 / 41Cr4, uni 41Cr4, SAE 41Cr4, 41Cr4, 41Cr4, 41Cr4, 41Cr4, 41Cr4, 41Cr4, 41Cr4 Amerika / ASTM Standard Steel Numera 5140, Iapani JIS uamea tulaga No. scr440 (H) / scr440, American AISI / SAE / ASTM Standard Steel Numera 5140, faalapotopotoga faava o malo mo Standardization ISO uamea tulaga No. 41Cr4.
(fa'atatau) ACM = 780 ℃
vevela 850 ~ 870 ℃, maaa 179 ~ 229hbs.
O le vevela o le 740 ~ 760 ℃, o le taimi e taofia ai o le 4 ~ 6h, ona fa'amalieina lea o le vevela i le ≤ 600 ℃ i le tau malulu o le 5 ~ 10 ℃ / h.
Malosi a'o le'i togafitia ≤ 217hbs, ma'a'a pe a uma ona fa'amalulu ≤ 163hbs.
(670 ± 10) ℃ × 2H, maualuga le vevela ma le ogaumu, (710 ± 10) ℃ × 2H, malulu i lalo ma le ogaumu, (670 ± 10) ℃ × 2H, maualuga le vevela ma le ogaumu, (710 ± 10) ℃ × 2H, ona faʻaititia lea o le vevela i le ogaumu, (670 ± 10) ℃ × 2H, maualuga le vevela ma le ogaumu, (710 ± 10) ℃ × 2H, faʻamalo i lalo ma le ogaumu mo le 3 taamilosaga, ona faʻafefe ai lea i lalo. 550 ℃ mo le mālūlū o le ea. Maaa pe a uma togafitiga e 153hbs.
Quenching vevela 850 ℃ ± 10 ℃, suauʻu malulu; Tempering vevela 520 ℃ ± 10 ℃, vai, suauʻu ma ea malulu.
Medium carbon modulated sila, maalili ulu uamea mate. O le uamea o loʻo i ai le tau talafeagai ma le faʻaogaina faigofie. A maeʻa togafitiga vevela talafeagai, e mafai ona maua ai ni faʻamaʻi, palasitisi ma le faʻaofuofu teteʻe. Normalizing e mafai ona faʻaleleia le spheroidization o le tino ma faʻaleleia le faʻatinoina o le tipiina o avanoa ma le maaa e itiiti ifo i le 160hbs. Faʻafefe i le 550 ~ 570 ℃, o le uamea o loʻo i ai mea sili ona lelei faʻainisinia. O le faʻamalosi o lenei uamea e maualuga atu nai lo le 45 sila. E fetaui lelei mo togafitiga faʻamaʻaʻaina e pei o le tineia o taimi maualuga ma le afi.
A maeʻa ona tineia ma faʻafefe, e faʻaaogaina lenei uamea e gaosia ai vaega faʻainisinia o loʻo i ai le mamafa o le mamafa ma le saoasaoa o le saoasaoa, e pei o le taʻavale faʻataʻitaʻi, pito i tua o le afa o le taʻavale, mea faʻaoga, mea, anufe, spline shaft, ogatotonu lima, ma isi mea i luga o meafaigaluega masini; A maeʻa le faʻafefeteina ma le vevela vevela, e faʻaaogaina e gaosia ai vaega o loʻo i ai le maualuga o le avega, aʻafiaga ma le saoasaoa o le saoasaoa, e pei o le mea e faʻaogaina ai, o le autu autu, suauʻu pamu rotor, poloka poloka, kola, ma isi; A maeʻa le faʻamalo ma le maualalo o le vevela, e faʻaaogaina e gaosia ai vaega o loʻo i ai le mamafa o le avega, maualalo le aʻafiaga, faʻafefeteina ma le mafiafia mautu i lalo ifo o le 25mm i luga o le vaega, e pei o anufe, ulu autu, faʻalava, kola, ma isi; A maeʻa ona faʻamalo ma faʻafefeteina ma faʻafefe maualuga, e faʻaaogaina e gaosia ai vaega e maualuga le maaa ma ofuina le tetee e aunoa ma se aʻafiaga tele, e pei o le mea e faʻaogaina, lima, faʻamau, faʻamau autu, crankshaft, spindle, pine, tootoo faʻafesoʻotaʻi, sikula, nut, inlet valve, ma isi. E le gata i lea, o lenei uamea e talafeagai foi mo le gaosiga o vaega eseese o felauaiga e togafitia e le carbonitriding, e pei o le faʻaogaina ma le paʻu ma le lapoa tele ma le malosi o le vevela maualalo.
Fa'amau, ma'a'a ≤ 207hbs. 40Cr fa'a'au'au fa'a'au'au: fa'atosina fa'alava E (20 ℃) / MPA 200000 ~ 211700, fa'atosina fa'alava G (20 ℃) 80800
Fa'agasologa o le tineia o le 40Cr
40Cr tineia, 850 ℃, suauʻu malulu; Tempering 520 ℃, vai malulu, suauʻu malulu. O le maaa tineia i luga o le paipa uʻamea 40Cr o le hrc52-60, ma o le tineia o le afi e mafai ona oʻo atu i le hrc48-55.
40Cr nitriding togafitiga
40Cr o le uamea uamea, ma o ona elemene e fesoasoani i le nitriding. 40Cr e mafai ona maua i luga o le maaa maualuga maualuga pe a uma togafitiga nitriding, ma le maaa sili ona maualuga pe a uma togafitiga nitriding e mafai ona oʻo atu i le hra72 ~ 78, ie hrc43 ~ 55. Nitriding workpiece auala faagasologa: forging annealing machining faigata tineia ma tempering maeʻa machining stress aveesea rough grinding nitriding faauma olo po olo. Talu ai ona o le nitrided layer e manifinifi ma malepelepe, e manaʻomia le i ai o se fausaga autu maualuga-malosi, o lea e tatau ai ona faʻataunuʻu ma faʻafefeteina le vevela togafitiga muamua e maua ai sorbite ita ma faʻaleleia mea faʻainisinia o le autu ma le lelei o le. o le nitrided layer. O le nitriding vaivai o le fa'atosina malosi, ma e masani ona fa'aogaina le fa'amalulu kasa
40Cr uelo
A'o le'i ueloina le 40Cr, fa'alogo lelei i le fa'avevela ina ia taofia ai le tineia o le ta'e i totonu o le uelo ona o le fa'amama o le vevela matrix. E sili atu le faʻavasegaina aʻo leʻi faʻapipiʻiina.
Uuleleia o le 40Cr: e faigofie ona tuueseeseina i le taimi o le tioata ma e maaleale i le tioata tioata (se ituaiga o vevela vevela). E faigofie ona ta'e i totonu o le lua ma vaega concave i le uelo i le taimi o uelo. Faatasi ai ma le maualuga o le carbon content, e faigofie ona maua le faʻamaʻaʻaina (martensite) lea e matua maaleale ile malulu malulu ile vave faʻafefe. Pe a tele le cooling fua o sone superheated, e faigofie ona fausia malosi ma brittle carbon martensite maualuga ma embrittle le sone superheated.
1. E masani ona fa'atinoina le uelo i totonu o le tulaga fa'alilolilo (normalized).
2. Le auala uelo e le faatapulaaina
3.O le vevela muamua e mafai ona fa'atuputeleina talafeagai ma le malosi laina tele. E masani lava, o le vevela preheating ma interlayer vevela e mafai ona pulea i le va o le 250 ~ 300 ℃.
4. O mea faʻapipiʻi e tatau ona faʻamautinoa o le tuʻufaʻatasia o le uamea ua teuina e tutusa lelei ma le uʻamea faavae, e pei o le j107-cr.
5.E tatau ona faia le tineia ma le fa'afefeteina o le vevela ile taimi pe'a uma le uelo. Afai e faigata ona faʻataunuʻu ma faʻafefe togafitiga i le taimi, faʻapipiʻi vavalalata poʻo le taofiofia i se vevela maualuga atu nai lo le faʻamafanafanaina mo se vaitaimi e mafai ona faia e faʻaumatia ai le hydrogen faʻasalalau ma faʻamalulu le fausaga. Mo oloa faʻapipiʻi lavelave ma le tele o uelo, e mafai ona faʻataunuʻuina le faʻaogaina o le vaeluaga pe a uma le faʻapipiʻiina o se numera o uelo.